铝板加工如何避免折弯开裂?

来源://www.renttoplux.com/发布时间:2022-03-15

铝板加工过程中常常会因为折弯而造成铝板断裂,尤其是折弯好后做阳极氧化处理的崩裂,更让许多铝板生产加工公司疑惑,那麼如何应对那样的问题产生呢,我们一起来剖析下铝板加工如何避免折弯开裂。
In the process of aluminum plate processing, aluminum plate fracture is often caused by bending, especially the cracking of anodizing treatment after bending, which makes many aluminum plate production and processing companies wonder, so how to deal with such problems? Let's analyze how to avoid bending cracking in aluminum plate processing.
造成铝板加工如何避免折弯开裂断裂缘故实际上关键下列这几个方面,如果我们在加工过程中留意下列问题,就会大大减少断裂的产生。


How to avoid bending cracking and fracture in aluminum plate processing actually depends on the following aspects. If we pay attention to the following problems in the processing process, the occurrence of fracture will be greatly reduced.
一. 铝板的强度太高。通常状况越硬的物件,越非常容易受外力作用危害断裂,铝板也是一样,因此我们在挑选铝板时一定要选好铝板,依据铝板型号和情况来挑选这些更非常容易折弯的商品,像铝板中1系列产品、3系列、5系列产品型号商品就很容易折弯,而6系列产品、7产品系列因为强度太高,必须做退火处理到O态后才好折弯。
I The strength of aluminum plate is too high. Generally, the harder the object is, the more likely it is to be damaged and broken by external force, and so is the aluminum plate. Therefore, when selecting the aluminum plate, we must select the aluminum plate, and select these products that are more easy to bend according to the aluminum plate model and situation. For example, the products of series 1, series 3 and series 5 in the aluminum plate are easy to bend, while the products of series 6 7 because the strength of the product series is too high, it must be annealed to o state before bending.
二.铝板的薄厚。铝板越厚越不容易折弯,和其它原材料一样,因此我们在挑选时,可以考量挑选薄铝板来生产加工商品,防止断裂产生。
II Thickness of aluminum plate. The thicker the aluminum plate, the less easy it is to bend. Like other raw materials, we can consider selecting thin aluminum plates to produce and process goods to prevent fracture.
三.折弯视角和铝板花纹。无论啥子物件折弯视角越大,通过率会越高,因此我们在铝板生产加工时,折弯视角尽量的大,再有就是铝板花纹,折弯方位要与铝板花纹方位竖直,不可以平行面。
III Bending angle and aluminum plate pattern. The larger the bending angle of any object, the higher the passing rate. Therefore, when we produce and process aluminum plate, the bending angle should be as large as possible. In addition, the aluminum plate pattern. The bending direction should be vertical with the aluminum plate pattern, and cannot be parallel.
在铝板加工如何避免折弯开裂过程中如果我们可以防止以上几个人难点,铝板折弯断裂的就会极大地降低,铝板生产厂家问题会获得不错的处理。
In the process of how to avoid bending cracking in aluminum plate processing, if we can prevent the above difficulties, the of aluminum plate bending fracture will be greatly reduced, and the problems of aluminum plate manufacturers will be well handled.