越来越多的铝板产品的金属外壳都使用了金属拉丝工艺，以起到美观，抗侵蚀的作用。使产品兼备时尚和科技的元素。这也是该工艺备受欢迎的原因之一，今天就跟着铝板生产厂家来了解一下铝板表面产生色差的因素有哪些。
More and more metal shells of aluminum plate products use metal wire drawing process to play a role of beauty and corrosion resistance. The product combines fashion and technology elements. This is also one of the reasons why this process is so popular. Today, let's learn about the factors that cause color difference on the aluminum plate surface.
1.染料溶液的温度：铝板的染色分为冷染和热染，冷染在生产过程中长期使用，对颜色均匀性有很好的把握。热染的使用是短暂的，但很难操纵颜色。热染色温度一般在40°C～60°C，如果温度过高，会减少染色的吸附，使铝板表面容易开花。
1. Temperature of dye solution: The dyeing of aluminum plate can be divided into cold dyeing and hot dyeing. Cold dyeing is used for a long time in the production process and has a good grasp of color uniformity. The use of hot dyeing is short-lived, but it is difficult to manipulate the color. The thermal dyeing temperature is generally 40 ° C~60 ° C. If the temperature is too high, the adsorption of dyeing will be reduced, making the aluminum plate surface easy to bloom.
2.对于氧化铝膜单板质量：氧化膜是指铝单板的厚度，孔隙率，透明度等，铝板氧化膜厚度可保持在10微米以上，可获得孔隙率和透明度，可获得较佳的染色质量。
2. For the quality of aluminum oxide film veneer: the oxide film refers to the thickness, porosity, transparency, etc. of the aluminum veneer. The thickness of the aluminum oxide film can be kept above 10 microns, so that porosity and transparency can be obtained, and better dyeing quality can be obtained.

3.浓度的染色液：染色溶液的浓度和的关系的染色。着色铝单板，较低的浓度，暗稍高浓度后。如果染料的较高浓度将颜色不均匀或浮色，在洗涤过程中容易地发生，并且在封闭的“彩色流”。为了提高染料的染料吸附能力，使用颜色的低浓度的延长染色时，染料分子渗透到更均匀的氧化膜的孔的深度，并且使颜色更和谐固体。
3. Staining solution of concentration: dyeing of the relationship between the concentration of dyeing solution and. Colored aluminum veneer, low concentration, dark slightly after high concentration. If the higher concentration of dye will cause the color to be uneven or floating, it will easily occur in the washing process, and in the closed "color flow". In order to improve the dye adsorption capacity of the dye, when the low concentration of color is used to extend the dyeing, the dye molecules penetrate into the hole depth of the more uniform oxide film, and make the color more harmonious solid.
4.影响的铝原料单板部分：一般情况下，高纯铝，铝镁，铝锰合金在生产过程中经过阳极氧化处理后，其染色性能好，可染成多种颜色，对于重硅或铜板，在染色过程中只能染成深色和黑色，颜色较为单调。
4. Affected aluminum raw material veneer: In general, high-purity aluminum, aluminum magnesium, and aluminum manganese alloys have good dyeing performance after anodizing in the production process, and can be dyed into a variety of colors. For heavy silicon or copper plates, they can only be dyed into dark and black during the dyeing process, and the color is relatively monotonous.
现在的铝板市场上,目前常见的铝板为了使其产品的表面装饰性变得更好，如果铝板的颜色效果不能达到理想的效果，它的应用将产生巨大的影响。所以说在生产使用前后要注重问题的预防，更多相关信息就来我们这里//www.renttoplux.com咨询吧！
In the current aluminum plate market, in order to make the surface decoration of its products better, if the color effect of aluminum plate can not achieve the desired effect, its application will have a huge impact. So we should pay attention to the prevention of problems before and after production and use. More relevant information will come to us //www.renttoplux.com Consult!